Materials for Turbine Power Blades, Reinforcements, and Resins - Hybrid Anisotropic Materials for Wind Power Turbine Blades - page 63

TABLE 3.5
Tensile.Properties.IM.Fiber.Unidirectional.Tape:.T40/800B.Impregnated.by.
Cycom.5320-1

IMFiber
Unidirectional TestMethod Condition Results

0°.Tension.
Strength,.ksi.(MPa).
Modulus.Msi.(GPa)

ASTM.D3039.
[0]8.

-100°F.(-73°C).DRY. 372.(2565).

22.6.(156).
0.258.

RTA. . 392.(2703).

22.7.(156).
0.344

90°.Tension.
Strength,.ksi.(MPa).
Modulus.Msi.(GPa).

ASTM.D3039.
[90]16.

-100°F.(-73°C).DRY. 12.1.(83).

1.6.(11.0).

RTA. 11.7.(81).

1.4.(9.7)

90°/0°.Tension.
Strength,.ksi.(MPa).
Modulus.Msi.(GPa).

ASTM.D3039.
[90,0]4S.

RTA. 190.(1310).

11.9.(82.0).

Unnotched.Tension.
Strength,.ksi.(MPa).
Modulus.Msi.(GPa).

ASTM.D3039.
[45,90,-45,0]3S.

-100°F.(-73°C).DRY. 124.(857).

8.5.(58.4).

RTA. 135.(931).8.4.

(57.6).

Filled.Hole.Tension
Strength,.ksi.(MPa)
Modulus,.Msi.(GPa)

ASTM.D6742
[45,0,-
45,0,0,45,90,-
45,0,.0,.
45,0,-45,0]S

-100°F.(-73°C).DRY 99.1.(683)

14.1.(97.2