Materials for Turbine Power Blades, Reinforcements, and Resins - Hybrid Anisotropic Materials for Wind Power Turbine Blades - page 64

TABLE 3.6
Compression.Properties

TestMethod
LayUp IMFiber Condition Results

0°.Compression.
Strength,.ksi.
(MPa).
Modulus.Msi.
(GPa).

SACMA.
SRM01R94.[0]8.

-100°F.(-73°C).
DRY.

270.(1862).
20.3.(140).

RTA. 220°F.(104°C) 252.(1737).

20.8.(143).

90°.Compression.
Strength,.ksi.
(MPa).
Modulus.Msi/
(GPa)

SACMA.
SRM01R94.
[90]16.

-100°F.(-73°C).
DRY.

56.9.(392).
1.7.(11.5).

90°/0°.
Compression.
Strength,.ksi.
(MPa).
Modulus.Msi.
(GPa).

SACMA.
SRM01R94.[90,.
0]4S.

RTA. 167.(1151).

10.9.(75.1).

Residual.
strength,.ksi.
(MPa).

ASTM.D7137.or.
SACMA.
SRM02R94.
[45,90,-45,0]4S

RTA 25.6.(176)

Open.Hole.
Compression.
Strength,.ksi.
(MPa).
Modulus,.Msi.
(GPa).

ASTM.D6484.
[45,.0,.-45,.0,.0,.
45,.90,.-45,.0,.0,.
45,.0,.-45,.0]S.

220°F.(104°C).
WET3.

56.0.(386).
13.8.(95.2)

Filled.Hole.
Compression.
Strength,..ksi.
(MPa)

ASTM.D6742.
[45,9.0,.-45,0]3S.

RTA 79.7.(550)

Table 3.7. represents. ˚the. shear. properties. IM. iber. unidirectional. tape:.
T40/800B.(Nominal.FAW.145.gsm;.nominal.resin.content.33.percent.by.weight).
Structural. Component. Manufacture. using. 8020. Rapi-Ply. Technology:.
www.ambercomposites.com.. Issue. Ref:. TDS/Page. 3. of. 7. RP8020/05. (July.
2009)..Rapi-Ply.is.available.in.a.wide.range.of.high.performance.reinforcing.
fabrics,.standard.conigurations.including:

Description.Rapi-Ply.Construction.Width.Molded.thickness
Carbon.fabrics
8020.RP.101.HS.Carbon.300.g/m 2 .2/2.twill.6K.43%/1.0.m.0.76.mm
HS.Carbon.300.g/m 2 .2/2.twill.6K.43%