TABLE 3.7
Shear.Properties.IM.Fiber.Unidirectional.Tape:.T40/800B
IMFiber
TestMethodLayUp
Condition
Results
Short.Beam.Shear.Strength,.
ksi.(MPa).
ASTM.D2344.
[0]16.
-100°F.(-73°C).
DRY.
23.8.(164)
RTA.
19.2.(132)
RTA
220°F.(104°C).
WET3.
11.3.(78)
Short.Beam.Shear.Strength,.
ksi.(MPa).
ASTM.D2344
.[0]30.
17.3.(119).
RTA
220°F.(104°C).
WET3.
11.6.(80)
In-Plane.Shear.Strength,.ksi.
(MPa).
Strength.at.0.2%.offset,.
1500-5500.mod.pt,.ksi.
(MPa).
Strength.at.0.2%.offset,.
500-3000.mod.pt.,.ksi.(MPa).
Modulus.1500.-.5500.μin/in,.
Msi.(GPa).
Modulus.500.-.3000.μin/in,.
Msi.(GPa).
ASTM.D3518.
[+45,.-45]2S.
RTA.
15.9.(110).
8.4.(58).
7.9.(54).
0.76.(5.2).
0.81.(5.6)
90°.Flexure.Strength,.ksi.
(MPa).
ASTM.D790.
[90]16.
RTA.
17.5.(121)
8020.RP.102.HS.Carbon.300.g/m
2
.2/2.twill.6K.43%/1.0.m.0.78.mm
HS.Carbon.285.g/m
2
.2/2.twill.12K.43%
8020.RP.103.HS.Carbon.300.g/m
2
.2/2.twill.6K.43%/1.0.m.1.14.mm
HS.Carbon.650.g/m
2
.2/2.twill.12K.43%
8020.RP.104.HS.Carbon.600.g/m
2
.2/2.twill.12K.40%/1.0.m.1.45.mm
HS.Carbon.650.g/m
2
.2/2.twill.12K.40%
Glass.fabrics
8020.RP.201.E.Glass.390.g/m
2
.2/2.twill.35%/1.0.m.0.7.mm
E.Glass.390.g/m
2
.2/2.twill.35%
8020.RP.202.E.Glass.300.g/m
2
.8HS.35%/1.0.m.0.55.mm
E.Glass.300.g/m
2
.8HS.35%
8020.RP.203.E.Glass.600.g/m
2
.PW.WR.35%/1.0.m.or.1.2.m.1.1.mm
E.Glass.600.g/m
2
.PW.WR.35%
8020.RP.204.E.Glass.450.g/m
2
.±45°.35%/1.27.m.0.88.mm
E.Glass.450.g/m2.±45°.35%
8020.RP.205.E.Glass.600.g/m
2
.8HS.35%/1.20.m.1.02.mm