incorporated into cellulose nanostructure by adjusting the homogenate to
alkaline pH. h e magnetic bacterial cellulose nanoi ber soaked in dopa-
mine solution will be coated with an adherent self-polymerized polydopa-
mine layer. Since the polydopamine surface is very ef ective for reducing
silver ion, silver nanoparticles were incorporated into the dopamine treated
magnetic bacterial cellulose by soaking in silver nitrate solution. h e mag-
netic silver nanocomposite possesses a high antimicrobial activity against
the model microbes Escherichia coli and Bacillus subtilis. It also has poten-
tial as a mild fermentation medium sterilizing agent that a freshly prepared
LB medium shows no appreciable contamination at er incubating with Ag
nanocomposite for 4 h and removed by an external magnet.
As it was already mentioned above, silver nanoparticles could be strong
bactericidal agents but they also can be cytotoxic. Embedding them in a
polymer matrix may reduce their cytotoxic ef ect. In the study of Liu et al,
silver nanoparticles in three average sizes were tested for their antibacterial
activities and cytotoxicity. Nanocomposites from a new waterborne poly-
etherurethane ionomer and silver nanoparticles were prepared without
the use of any crosslinker. It was observed that the antibacterial activity of
silver nanoparticles against Escherichia coli started at the ef ective con-
centration of 0.1-1 ppm, while that against Staphylococcus aureus started
at higher concentrations of 1-10 ppm. Cytotoxicity of silver nanoparticles
was observed at the concentration of 10 ppm. Silver nanoparticles with
smaller average size showed greater antibacterial activity as well as cyto-
toxicity. h e PEU synthesized in this study showed high tensile strength,
and the addition of AgNPs at all sizes further increased its thermal stability.
h e delicate surface features of nanophases, however, were only observed
in nanocomposites with either small- or medium-sized AgNPs. PEU-Ag
nanocomposites had a strong bacteriostatic ef ect on the growth of E. coli
and S. aureus. h e proliferation of endothelial cells on PEU-Ag nanocom-
posites was enhanced, whereas the platelet adhesion was reduced. h e
expression of endothelial nitric oxide synthase gene was upregulated on
PEU-Ag containing small-sized AgNPs (30 ppm) or medium-sized AgNPs
(60 ppm). h is ef ect was not as remarkable in nanocomposites from large-
sized AgNPs. Overall, nanocomposites from the PEU and 60 ppm of the
medium-sized (5 nm) AgNPs showed the best biocompatibility and anti-
bacterial activity. Addition of smaller or larger AgNPs did not produce as
substantial an ef ect in PEU, especially for the larger AgNPs.
Vimala
et al
have reported the preparation of semi interpenetrating
hydrogel networks (SIHNs) based on cross-linked poly (acrylamide) pre-
pared through an optimized rapid redox-solution polymerization with
N,N -methylenebisacrylamide in presence of three dif erent carbohydrate