These ''carbyne'' crystals were surrounded by disordered diamond crystals
(
Figure 5.2(a)
)
. The film thickness was determined from SEM observation,
and was about 15
m
m. EDX analysis shows that the deposited films were
constituted of pure carbon (Figure 5.2(b)).
5.3.1.2 Carbon Film Deposited at
s ¼
1.1
Crystals with a hexagonal form assigned to ''carbyne'' or ''tetragonal''
crystallized diamond were observed (Figure 5.3(a)). The film's texture was
constituted of small crystals. The average crystal size is about 1-2
m
m. These
crystals were surrounded by diamond crystals. The film thickness was about
10
m
m. EDX analysis shows that the deposited films were constituted of pure
carbon (Figure 5.3(b)).
FIGURE 5.3
SEM image and EDX analysis of carbyne film obtained by the
combustion flame method;
¼
1.1.